Product Description

HBE308L-16

Accord to AWS E308L-16

 

The 0.04 percent maximum carbon content of weld metal deposited by HBE308L-16 reduces the possibility of intergranular carbide precipitation and thereby increases the resistance to intergranular corrosion without the use of stabilizers such as columbium (niobium) or titanium.

A carbon content of 0.04 percent maximum has been shown to be adequate in weld metal, even though it is

recognized that similar base metal specifications require a 0.03 percent limitation. This low carbon alloy.

 

Used for welding corrosion-resistant stainless steel

 

Chemical Analysis：%

	C	Mn	Si	S	P	Cr	Ni	Mo	Cu
Typical	0.04	0.5-2.5	1.00	0.03	0.04	18-21	9-11	0.75	0.75

Mechanical Property

	T.S Rm(MPa)	Y.S ReH(MPa)	Elongation A(%)	Impact AKV(J)	［H］ml/100g
Typical	520	-	35	-	-

 