HBE309L-16
Accord to AWS E309L-16
The 0.04 percent maximum carbon content of these weld deposits reduces the possibility of intergranular carbide precipitation and thereby increases the resistance to intergranular corrosion without the use of stabilizers such as columbium (niobium) and titanium.
Used for welding 0Cr21Ni10 and 0Cr17Ni12Mo2 stainless steel structures.
Chemical Analysis：%
|
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
Mo
|
Cu
|
|
Typical
|
0.04
|
12-14
|
1.00
|
0.03
|
0.04
|
22-25
|
12-14
|
0.75
|
0.75
|
Mechanical Property
|
|
T.S
Rm(MPa)
|
Y.S
ReH(MPa)
|
Elongation
A(%)
|
Impact
AKV(J)
|
［H］ml/100g
|
|
Typical
|
520
|
-
|
30
|
-
|
-
|
Package:
2kgs in one plastic tube
10 tubes in one carton