HBENiFe-CI
in accordance with AWS A5.15 ENiFe-CI
Used for welding of high-hardness grey cast iron and graphite cast iron as well as for joining cast irons to mild steels.
It is also readily used for the repair of castings.
The welds are moderately hard and require carbide tipped tools for machining.
A preheat and inter-pass temperature of not less than 350° is required during welding to prevent cracking.
Chemical Analysis：%
|
|
C
|
Mn
|
Si
|
S
|
Ni
|
Fe
|
|
Requirements
|
≤2.0
|
≤2.50
|
≤4.0
|
≤0.03
|
45-60
|
Bal
|
|
Typical
|
0.11
|
0.95
|
1.83
|
0.012
|
52.50
|
Bal
|
Typical parameters:
|
Diameter(mm）
|
2.5
|
3.2
|
4.0
|
5.0
|
|
Length(mm）
|
300
|
350
|
400
|
400
|
|
Amperage（A）
|
Flat
|
60-90
|
90-130
|
150-180
|
180-210
|
|
Vertical & Overhead
|
50-80
|
80-110
|
120-150
|
150-190
|
Welding Current AC - DC
Welding Positions F,V,OH
Typical Applications
• Cast iron
• Graphite cast iron
• Machine parts
• joining cast iron to mild steel
Notice:
1)Heating 2 hour at 350℃ in oven prior to welding
2)Remove all unclean staffs,oil,water,rust on surface prior to welding.。