HBE316L-16
Accord to AWS E316L-16
The 0.04 percent maximum carbon content of weld metal deposited by these electrodes reduces the possibility of intergranular carbide precipitation and thereby increases the resistance to intergranular corrosion without the use of stabilizers such as columbium (niobium) or titanium.
is used principally for welding low carbon, molybdenum-bearing austenitic alloys.
Tests have shown that 0.04 percent carbon limit in the weld metal gives adequate protection against intergranular corrosion in most cases.
Used for welding OCr17Ni12Mo2stainless steel suitablefor organic and inorganic acid medium.
Chemical Analysis：%
|
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
Mo
|
Cu
|
|
Typical
|
0.04
|
0.5-2.5
|
1.00
|
0.03
|
0.04
|
17-20
|
11-14
|
2-3
|
0.75
|
Mechanical Property
|
|
T.S
Rm(MPa)
|
Y.S
ReH(MPa)
|
Elongation
A(%)
|
Impact
AKV(J)
|
［H］ml/100g
|
|
Typical
|
490
|
-
|
30
|
-
|
-
|
Package:
2kgs in one plastic tube
10 tubes in one carton